Characterization of the micro-contaminants from the inner-body of Kraak porcelain excavated from the "Nan'ao I" shipwreck, the South China Sea

doi:10.1186/s40494-019-0328-0

IVPP-IR > 中科院古脊椎所（2000年以后）

	Characterization of the micro-contaminants from the inner-body of Kraak porcelain excavated from the "Nan'ao I" shipwreck, the South China Sea
	Du, Jingnan 1,2,3; Luo, Wugan 2,3,4; Li, Naisheng 5; Wang, Changsui 2,3
	2019-10-22
发表期刊	HERITAGE SCIENCE
ISSN	2050-7445
卷号	7 期号:1 页码:9
通讯作者	Luo, Wugan(xiahua@ucas.ac.cn)
摘要	In this paper, optical microscopy, SEM-EDS, Raman and FT-IR analyses were used to investigate different types of corrosion product between layers of glaze and body of Kraak porcelain objects that were excavated from "Nan'ao I" shipwreck, the South China Sea. Several contaminants including NaCl, CaSO4 center dot 2H(2)O, FeOOH and FeS2, were found in many of the pores and cracks of the porcelain objects from Jingdezhen Kiln and Zhangzhou Kiln, even after conservation. While compared with the sample of Jingdezhen Kiln, the contaminants in the sample of Zhangzhou Kilns much more severely. The research pointed out that these contaminants were formed due to the marine environment influence and cross-contamination with other metal relics located in the shipwreck, and more contaminants formed in porous structure, hence reduce the porcelain quality. As regards to conservation, the fragility of ceramic objects from underwater contexts are likely to be caused by various kinds of insoluble ferrous salts and its phase transition pressure. Previous studies on this kind of remains tend to focus on the macro-insoluble salts on the enamel surface. In this paper, preliminary investigations were performed for the first time on different kinds of inner micro-corrosion product in China.
关键词	Underwater porcelain Micro-contaminants The "Nan'ao I" shipwreck
DOI	10.1186/s40494-019-0328-0
关键词[WOS]	HIGH-PRESSURE ; RAMAN ; DESALINATION ; TRANSITION ; MINERALS ; SULFUR
收录类别	SCI
语种	英语
资助项目	University of Chinese Academy of Sciences[2019-Y954026XX2] ; Youth Innovation Promotion Association of CAS ; National Scholarship Fund of China (CSC)[201404910198] ; National Natural Science Foundation of China[41471167] ; National Social Science Fund of China[13BKG004]
项目资助者	University of Chinese Academy of Sciences ; Youth Innovation Promotion Association of CAS ; National Scholarship Fund of China (CSC) ; National Natural Science Foundation of China ; National Social Science Fund of China
WOS研究方向	Arts & Humanities - Other Topics ; Chemistry ; Materials Science ; Spectroscopy
WOS类目	Humanities, Multidisciplinary ; Chemistry, Analytical ; Materials Science, Multidisciplinary ; Spectroscopy
WOS记录号	WOS:000492187800001
出版者	SPRINGEROPEN
引用统计
文献类型	期刊论文
条目标识符	http://119.78.100.205/handle/311034/16919
专题	中科院古脊椎所（2000年以后）
通讯作者	Luo, Wugan
作者单位	1.Northwestern Polytech Univ, Sch Mat Sci & Engn, Xian, Shaanxi, Peoples R China 2.Univ Chinese Acad Sci, Sch Humanities, Dept Archaeol & Anthropol, Beijing, Peoples R China 3.Chinese Acad Sci, Inst Vertebrate Paleontol & Paleoanthropol, Key Lab Vertebrate Evolut & Human Origin, Beijing, Peoples R China 4.Univ Missouri, Res Reactor Ctr, Columbia, MO USA 5.Chinese Acad Cultural Heritage, Beijing, Peoples R China
推荐引用方式 GB/T 7714	Du, Jingnan,Luo, Wugan,Li, Naisheng,et al. Characterization of the micro-contaminants from the inner-body of Kraak porcelain excavated from the "Nan'ao I" shipwreck, the South China Sea[J]. HERITAGE SCIENCE,2019,7(1):9.
APA	Du, Jingnan,Luo, Wugan,Li, Naisheng,&Wang, Changsui.(2019).Characterization of the micro-contaminants from the inner-body of Kraak porcelain excavated from the "Nan'ao I" shipwreck, the South China Sea.HERITAGE SCIENCE,7(1),9.
MLA	Du, Jingnan,et al."Characterization of the micro-contaminants from the inner-body of Kraak porcelain excavated from the "Nan'ao I" shipwreck, the South China Sea".HERITAGE SCIENCE 7.1(2019):9.